Phenolic Resin Reinforcing Kevlar Strands

Model NO.: XGPF1220
Width: 1.2D
Function: High Strength Fiber
Structure: Miscellaneous Chain Synthetic
Model: Xgpf1220
Colors: Yellowish
Fiber: PARA-Aramid
Density: 1.47g/cm3
P-Aramid Content: 100%
Average Fiber Length: 20mm
Tensile Strength: 19.4-21 Cn/Dtex
Tensile Modulus: 80gpa~120gpa
Elongation at Break: 2.5%-3.84%
Moisture: <0.2%
Trademark: XIANGU
Transport Package: 5kg Per Bag
Specification: ROHS
Origin: Guangdong
HS Code: 54021190
20mm phenolic resin reinforcing kevlar strands was chopped in 20mm by a special cutting equipment. This fiber has high strength and modulus, strong hydrogen bonding strength, strength up to 28 g/d or more, strength is 5-6 times of steel wire.specific modulus 2-3 times of it,toughness 2 times of it while weight is just 1/5 of the wire.Continuous using temperature range is extremely wide, long running in the range of -196 ºC to 204 ºC,no decomposition and melting at high temperature of 560 ºC,strength can maintain 75% through 100 hours at 200 ºC.also has good chemical solvent resistance, resisting acid and alkali, anti-aging, good adhesion to rubber. Usually it is used as a reinforcing material in the fields of thermoplastics, thermosetting plastics, high-temperature composite structures, brake pads, clutch linings, friction material, wear-resistant filler, cable sheathing, gaskets, slot insulation, phase insulation barrier, interturn insulation and so on.
 
SPECIFICATIONS:
Model: XGPF1220
Color: yellowish
Fiber type: Para-aramid
Density(g/cc) 1.47
Linear density of mono filament(D)  1.5
Filament diameter(μm) 12
Fiber length(mm) 20
Tensile strength( cN/dtex) 19.4-21
Elongation at break(%) 2.5-3.84
Tensile modulus(GPa) 80~120
Shrinkage(%) <0.2(190ºC×15m)
Moisture (%): <0.2

APPLICATION FIELDS:
1.Engineering Plastics,thermosetting resin,friction materials, automotive brakes,composite materials and Kevlar reinforced paper. 
2.reinforcing materials,construction,rubber,reinforced cable,cable and other high-intensity rope.
3.composite material with resin or rubber,can significantly reduce the weight,increase loading weight,suitable for the production of aerospace equipment,high-speed trains and yachts shell.
4.Friction and sealing materials,friction materials reinforced fiber, significantly improved wear resistance,suitable for high temperature conditions.
 
STORAGE:
The 20mm phenolic resin reinforcing kevlar strands should be keep dry in their original bags and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner black plastic film bags,net weight 5.00kg.gross weight 5.20kg.
2.Bag size:43*36*28cm,net weight 120.00kg.gross weight 150.00kg.

SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 20 pallets(each 180kg.two layers)be loaded into 20 feet container.total net weight is 2400kg.
2.transportation by truck:for truck transportation,generally loading in buck with 7layers,about 3120kg
3.transportation by rail:for rail transportation,generally loading in buck,about 6720kg.
 

Zipper Parts

Zipper parts can include a variety of items such as zipper pulls, Zipper Stops, zipper sliders, zipper tabs, zipper guards, zipper coils, zipper teeth, and zipper tape. Zipper pulls are the most common type of zipper accessory, and they are used to help open and close the zipper. Zipper stops are used to keep the zipper from coming undone, while zipper sliders are used to adjust the size of the zipper opening. Zipper tabs are used to attach the zipper to the fabric and zipper guards are used to protect the fabric from the zipper teeth. Zipper coils are used to give a decorative look to the zipper, while zipper teeth are used to hold the fabric together. Lastly, zipper tape is used to reinforce the zipper and keep it from unraveling.

zipper slider,zipper puller,zipper stops,zipper tape,zipper parts

RR Zipper , https://www.rrzipper.com